SGS bimetal contact

Detailed Product Description

SGS Bi-metal Electrical Contacts

material:  Ag/Cu, AgZnO8/Cu,AgNi/Cu, AgSnO₂/Cu, AgSnO₂In₂O₃/Cu, AgCu/Cu, /Cu,  etc.

material	composition	Density g/cm3	Resistivity μΩ. cm	Hardness HV kg/mm3
Ag	≥99.95	≥10.49	≤1.6	30--70

 

Material	composition		Density   g/cm3	Resistivity μΩ. cm	Hardness HV kg/mm3
	Ag	ZnO
AgZnO8	92	8	9.70-10.05	3.20	65-100
AgZnO10	90	10	9.50-9.85	3.40	70-120

 

Material	Conposition		Density g/cm3	Resistivity μΩ. cm	Hardness HV kg/mm3
	Ag	Ni
AgNi10	90	10	10.00-10.32	≤2.10	50-100
AgNi20	80	20	9.80-10.15	≤2.30	60-110
AgNi30	70	30	9.70-9.97	≤2.70	80-115
AgNi40	60	40	9.50-9.81	≤3.40	82-130

 

material	composition			Density g/cm3	Resistivity μΩ. cm	Hardness HB Mpa
	Ag	SnO2	In2O3
AgSnO2(8)In2O3(4)	88	8.0	4.0		≤3.40	750-1275
AgSnO2(10)In2O3(4)	86	10.0	4.0	9.70-10.05	≤3.50	820-1325

Pure silver contact:

Features:

(1) Pure silver has extremely high electrical conductivity

(2) Very low contact resistance

(3) Easy to solder

(4) It is easy to produce, so silver is an ideal contact material

(5) It is one of the most widely used materials in small capacity and voltage

AgNi contact:

Features:

(1) AgNi contact material contains 10% to 40% Ni

(2) Produced by powder metallurgical production, with low and stable contact resistance,
high hardness and mechanical strength
(3) Material transfer in case of DC is very low

(4) High electrical and thermal conductivity

(5) With very low arc erosion. On making higher current, normally asymmetric pairs
with AgC contact materials are applied(

6) Wire of solid and composite rivets produced by powder sintering-extruding methods

AgSnO2 contact

:Features:

(1) AgSnO2 is the ideal material of AgCdO and has excellent properties of contacts
(2) AgSnO2 has higher thermal stability

(3) AgSnO2 has higher resistance against welding and erosion than AgCdO material
(4) Non-poisonous. So it is a new material which is empoldered and developed actively over the world

(5) For AgSnO2 contact material, the contact resistance can be controlled within
thelimited range by putting in a small amount of additive of special metal-oxide
(6) In this aspect, contact materials produced by powder metallurgy processing method have higher resistance against arc erosion and less arc bumming than those produced by oxidation processing method

AgZnO contact rivet

Features:

(1) ZnO, one type of material in AgznO contact, has comparatively higher thermalstability

(2) The welding resistant and resistance against arc erosion of the contact making
ZnO material a higher product

(3) The AgZnO contact material has higher welding resistance and low arc erosion
with strong magnetic arc blowing under large switching capacity

(4) AgZnO contact material is innocuous and has no pollution to the environment

(5) AgZnO contact material is mostly suitable for contactors and circuit breakerswith